Board level vibration testing is intended to assess prediction of the reliability of solder joint interconnects that are formed between electronic components and printed circuit boards (PCB). Frailties in the stress test experiment might lead to false board level reliability (BLR) evaluations. Therefore, it is essential to have a well-characterized board level vibration test method. Currently, there is no industrial test standard that prescribes board level vibration test method for electronic components at the PCB level. This paper examines the vibration test standards that are currently available in the industry and their applicability at the solder joint interconnect level. Next to that, it surveys the state-of-the-art board level vibration test setups and their impact on PCB dynamic loading and reliability at solder joint-PCB interface. It collates research on major building blocks of a board level vibration test method that includes vibration measurement techniques, PCB assemblies under test, board mounting schemes, operating environments, fault detection systems, and vibration test stress conditions that are currently used in the domain of solder joint level vibration testing. The findings from this paper are expected to reveal pitfalls and challenges while setting up board level vibration test experiments for electronic components. In addition, this paper attempts to identify research efforts that are required to make board level vibration testing a more credible means for assessing solder joint reliability. Outcomes from this study can further be used to guide future board level vibration specifications for electronic components.@en

The risk of corrosion poses a challenge to meet the stringent reliability requirements of microelectronic devices that are used in harsh environments. Microelectronic devices are often encapsulated in polymer packaging materials, which protect them from corrosion. These polymers are, however, not completely hermetic and thus allow small amounts of ions and moisture to reach the device, which might cause corrosion of the microelectronic circuitry. To improve and predict the reliability of the device, it is important to quantify the ion diffusivity in these materials. Previously reported values for the ion diffusivity vary by multiple orders of magnitude for a single class of material. Here, we investigate the causes for this discrepancy using three experimental methods: (i) saltwater immersion, (ii) diffusion cell measurements, and (iii) transient electric current measurements. Several materials, such as silicone, epoxy, and polyamide, were tested to cover the broad spectrum of polymers used by the microelectronics industry. We found that the discrepancies are likely due to the strong dependence of the ion diffusivity on both the moisture content within the polymers, as well as on the salt concentration and pH of the solutes. Furthermore, we found that the very low ion diffusivity causes long measuring times, and thus a large risk for errors from contamination, leakage, or minor defects in the samples.@en

Epoxy Mold Compounds (EMC) are used to protect integrated circuits (IC) from environmental influences, with one of these influences being moisture ingress, causing corrosion. To obtain the needed thermal and mechanical properties EMCs require a high loading of (silica) fillers, introducing a large amount of interface. While silane coupling agents promote good binding, they have shown to introduce an interphase volume that exhibits a faster moisture transport between epoxy and SiO2 in glass fiber filled epoxy. In this work, we investigate if such an interphase volume is also introduced by the filler particles in EMC and if it influences the moisture diffusion coefficient of the composite. We compare moisture uptake measurements performed by dynamic vapor sorption (DVS) with predictions from effective medium theory, as well as with numerical simulations based on micro-CT scans of our samples for a model epoxy system containing different filler levels and commercial EMC samples with two different filler levels. From the measured DVS data, we observe an effective diffusion coefficient, that is higher than predicted for an absence of any interphase for both the EMC and the model system. This suggests that an interphase layer should be present.@en