The majority of bridges and quay walls in the centre of Amsterdam are supported by 100–300 years-old wooden foundation piles subjected to bacterial decay. Bacterial degradation proceeds at a slow rate, allowing the piles to perform their function for many years, although causing a reduction of their load-carrying capacity over time. In this study, micro-drilling measurements were employed to capture the amount of decay and remaining short-term compressive strength of the historic wooden piles. The applicability of micro-drilling was studied on 60 wooden piles with various decay levels, retrieved after 100–295 years of service life. An algorithm was developed for analysing the micro-drilling signals, aimed at determining the decayed outer layer of the piles’ cross section, and validated with the results of mechanical testing on the piles. The micro-drilling technique is now used on a large scale in Amsterdam, supporting the assessment of the wooden foundation piles in the city.

This case study explores the utilization of distributed fiber optic sensors (DFOS) in wooden foundation piles, for assessing and monitoring the stress distribution along their length. Three spruce and three pine foundation piles instrumented with DFOS were driven into the soil in a testing field in Amsterdam and axially loaded in compression. Since DFOS provided strain information, calculating the stress distribution in the piles required knowledge of their stiffness properties, which inherently vary from the head to the tip. Consequently, the piles were extracted and their overall wet dynamic elastic modulus (E_c,0,dyn,wet) was determined through frequency response measurements. Subsequently, the piles were segmented, transported to the TU Delft Laboratory and subjected to mechanical testing. For each segment, the mechanical properties were determined and their variability along the pile was studied, in particular for the static modulus of elasticity (E_c,0,stat,wet). This enabled a comprehensive assessment of the actual in-situ stress distribution (Δσ_actual,stat and Δσ_actual,dyn) along the length of the piles, calculated with DFOS strains and the pile stiffness (E_c,0,stat,wet and E_c,0,stat,dyn). Given the novelty of the DFOS application to timber piles, a validation of the accuracy was conducted on 3 pile segments equipped with DFOS. These segments underwent laboratory compression testing, allowing for a direct comparison between DFOS strain readings and strains measured with linear potentiometers attached to the pile segments. The results revealed good accuracy of DFOS in controlled lab conditions, with a maximum stress deviation of 0.65 MPa. Since the testing field featured a 6-meter-deep predrilled layer, where negligible shaft friction was mobilized, the no-friction stress (Δσ_no-friction) approximately aligned with Δσ_actual,stat on the piles. At pile tips, the maximum applied 300–350 kN compressive load (i.e. Δσ_no-friction = 20–26 MPa), resulted in Δσ_actual,stat = 4–7 MPa, highlighting shaft friction effect. The calculated Δσ_actual,dyn with a single E_c,0,stat,dyn for the whole pile, led to 3 MPa stress overestimation at pile tip. Although this calculation is conservative, the detailed knowledge of the variation of stiffness properties along the pile would result in a more efficient structural use.

In the historic city centre of Amsterdam (NL), the predominant foundation system is comprised of wooden piles. Due to their placement below the water table, these foundations are susceptible to bacterial decay. This study aims to investigate and compare various methods for characterizing decay patterns within the cross sections of piles retrieved from two bridges in Amsterdam. The examined piles span different construction years: three originate from 1727, four from 1886, and two from 1922. Following extraction, the piles were transported to TU Delft Stevin II Laboratory, where they underwent further subdivision into three segments, each representing the head, middle, and tip, resulting in a total of 27 segments. The effects of bacterial decay were characterised by performing micro-drilling measurements, small-scale material and compressive tests on prismatic samples extracted from the segments' cross sections, computed tomography scans, and light microscopy observations. Microscopic examination revealed severe degradation in all segments dating back to 1727, extending 20–50 mm from their surface. This outcome was also confirmed by the other adopted methods: the corresponding prisms had large moisture contents and poor mechanical properties, while low basic densities and drilling amplitudes were obtained from CT scans and micro-drilling measurements, respectively. On the contrary, the internal sections of the 1727 segments exhibited no evidence of decay and demonstrated properties consistent with those observed in sound segments from 1886 and 1922. Finally, the observed gradients of density, strength, and stiffness were well correlated with micro-drilling measurements, which can therefore be reliably used as on-site assessment method to reconstruct the properties of the piles.

In the historic city centre of Amsterdam (NL), the most widespread foundation system consists of wooden piles. With the aim of modelling and predicting remaining service life of these foundations and the piles in particular, one of the possible methods for collecting data and monitoring their condition consists of micro-drilling (MD) measurements. This work evaluates the reliability of MD measurements in identifying decayed portions and specific features of wooden foundation piles, considering different moisture content (MC) values. To this end, 24 segments were selected, sawn from wooden piles extracted from site, and having time in service (TS) of 2 to 294 years (with reference to 2021, the year of extraction). 240 MD measurements were conducted at varying MC values of 7% to 212%. The obtained MD profiles showed for all TS a slight decrease in drilling resistance when increasing MC. However, from the MD signals it is possible to reliably detect the areas affected by biodegradation phenomena (e.g. bacterial decay) along the drilling depth, regardless the MC of the segment or its gradient along the drilling depth. The present study contributes to research aiming at utilizing (in-situ) MD techniques for reliably assessing and quantifying decay and to be used in remaining service life planning of wooden foundation piles.

This work investigated the influence of knots on the compression strength of wooden foundation piles. The study involved 110 pile segments sawn from 18 spruce and 9 pine piles with a mean diameter of approximately 200 mm, and moisture contents above fiber saturation. The mechanical properties were determined performing both full-scale compression tests on pile segments, and small-scale experiments on discs sawn from selected segments, considering samples with and without knots. A knot ratio (KR) was defined analysing the knots layout of each wooden pile, and evaluating how the compressive strength was influenced by size, number and layout of knots. As final step, a prediction model was implemented based on the dry density and KR of wooden piles, to estimate the influence of knots on their compressive strength.

Timber pile foundations are widespread in many areas around Europe and North-America. Especially in areas with weak soils, timber pile foundations have been a very good and economic solution. However, aging of the foundations can become a problem, as physical, biological and/or chemical degradation may occur over time. Now, that foundations can be up to 500 years in cities like Venice, Amsterdam, Hamburg, Boston and many others, questions arise about the reliability and which assessment methods can be used in order to estimate the current load carrying capacity and their residual service life. Residual service life is depending both on the time-to-failure behaviour of wood, as well as, the dead and live loads on the piles below buildings, quay walls and bridges. The approach taken integrates degradation models with a reaction kinetics based damage model. For wood that remains consistently below the waterline, the combination of bacterial degradation and long term loading is considered the most important, but degradation by fungi also may occur depending on soil and groundwater conditions. The integral assessment model will function as a tool for repair and maintenance strategies for asset managers and structural engineers.