Driven by the energy transition and the reduction of carbon emissions, pultruded CFRP plates have emerged as an affordable high performance material for designing wind turbines with larger rotors. To enable the creation of thicker laminates, pre-cured plates are bonded together u ...
Laminated pultruded composite plates are gaining interest for use in wind turbine blades due to their excellent structural performance with affordable cost. However, there is limited understanding of their fracture properties. The present work explores the interlaminar fracture b ...

This paper presents the results of an experimental campaign carried out to characterise the mechanical properties of multi-wythe masonry infrastructure in the city of Amsterdam. Samples were extracted from a 1.2 m thick bridge’s pillar constructed in 1882. For the characterisa ...

The present work aims at understanding the stochastic matrix crack evolution in CFRP cross-ply laminates under tension–tension fatigue loading. An experimental campaign was carried out on twenty-three specimens at different stress levels, while two optical techniques were used ...

The present work aims at providing insights on the material characterization of multi-wythe masonry infrastructure, in particular exploring a through-thickness effect of mechanical properties and benchmarking the core testing as an efficient slightly-destructive testing method ...

Numerical modelling of ice

Mechanical behaviour of ice under high strain rates

Ice impact is quite common and may become critical especially if it involves the transportation sector. Simulation tools may help in the structural design phase to increase the ability to withstand this kind of impact and/or to analyse the effect under extreme weather conditio ...

Foamed concrete is an essential material in engineering that can be categorized into two types based on density distribution, namely uniform foamed concrete (UFC) and gradient foamed concrete (GFC). However, there exists a research gap concerning the mesoscopic deformation mec ...

Ply-block size and stress level effect on accumulation of transverse cracks and delamination are investigated during early fatigue life of CFRP laminates. Tension-tension fatigue tests under different stress levels were performed for two cross-ply configurations. Edge observat ...

The present work aims at investigating the progressive damage accumulation process of CFRP laminates in an interactive scheme, with a special focus on the early fatigue life where mainly matrix-dominant damage accumulates and stiffness degrades significantly. An in-situ damage mo ...

Rain erosion may cause substantial damage to aircrafts during supersonic flight. Such event is investigated here via high-speed waterjet impact on composite laminates. An experimental setup is developed to produce waterjets with the speed up to 700m/s and a finite element mode ...

Fatigue damage of composite laminates has attracted considerable attention from research community and industry, in view that laminated structures are inevitable to suffer from fatigue loading during their service life. It is rather complicated to understand and explain, what gov ...
This paper investigates the loading rate effect on both mechanical properties and damage accumulation process of [0°2/90°4]S carbon fiber-polymer laminates under tensile loading. In-situ edge observations, Acoustic Emission and Digital Image Correlation techniques were utilized s ...

Carbon fiber-reinforced composite materials are widely employed in aircraft structures due to their high specific strength and high specific modulus. However, the poor impact resistance of carbon fiber reinforced composites creates challenges for aircraft design and maintenanc ...

This study investigates the early fatigue damage of cross-ply carbon/epoxy laminates. The aim is to unfold the damage accumulation process, understand the interaction between different damage mechanisms, and quantify their contribution to stiffness degradation. Tension-tension ...

The mechanical characterization of textile composites is a challenging task, due to their nonuniform deformation and complicated failure phenomena. This article introduces a three-dimensional mesoscale finite element model to investigate the progressive damage behavior of a no ...