Here, we investigated the separate and combined effects of guanidinium (Gua⁺) and/or thiocyanate (SCN⁻) ions on the opto-electronic properties of mixed Sn–Pb perovskites, which are used as absorber layers in photovoltaics. Therefore, we spin-coated Cs_0.25FA_0.75Sn_0.5Pb_0.5I₃ thin films with GuaI, Pb(SCN)₂ or GuaSCN, in the absence or presence of SnF₂. By comparing the (micro)structural and opto-electronic properties of the perovskite films, we elucidated the functions of both ions. We found that SCN⁻ suppresses tin oxidation and doping, reduces crystal defects and improves the carrier transport properties, regardless of SnF₂ addition. We demonstrate that this is due to coordination with Sn²⁺ and scavenging of Sn⁴⁺ in the spin-coating solution, resulting in a pile-up of SnO_x at the film surface. Gua⁺ is incorporated to a limited extent into the 3D cubic perovskite structure. Gua⁺ cannot suppress tin oxidation and doping, making this additive useless without SnF₂. Conversely, when combined with SnF₂, Gua⁺ enhances the carrier transport properties. Combining Gua⁺ and SCN⁻ until a maximum addition of 4 mol% and SnF₂ results in large grains and pinhole-free films with superior charge carrier transport properties, leading to a substantial increase in the pseudo-open circuit voltage of 50 mV. Addition of >4 mol% GuaSCN leads to the formation of Gua-based 2D perovskites, including Gua_xFA_2−xSn_yPb_1−yI₄ and Gua_xFA_3−xSn_yPb_2−yI₇, which do not improve the carrier dynamics. In short, we observe a synergistic effect on addition of Gua⁺ and SCN⁻ ions, which leads to improved structural and opto-electronic properties, which is promising for implementation in solar cells.

State-of-the-art triple cation, mixed halide perovskites are extensively studied in perovskite solar cells, showing very promising performance and stability. However, an in-depth fundamental understanding of how the phase behavior in Cs_0.05FA_0.85MA_0.10Pb(I_0.97Br_0.03)₃ (CsMAFA) affects the optoelectronic properties is still lacking. The refined unit cell parameters a and c in combination with the thermal expansion coefficients derived from X-ray diffraction patterns reveal that CsMAFA undergoes an α–β phase transition at ≈280 K and another transition to the γ-phase at ≈180 K. From the analyses of the electrodeless microwave photoconductivity measurements it is shown that shallow traps only in the γ-phase negatively affect the charge carrier dynamics. Most importantly, CsMAFA exhibits the lowest amount of microstrain in the β-phase at around 240 K, corresponding to the lowest amount of trap density, which translates into the longest charge carrier diffusion length for electrons and holes. Below 200 K a considerable increase in deep trap states is found most likely related to the temperature-induced compressive microstrain leading to a huge imbalance in charge carrier diffusion lengths between electrons and holes. This work provides valuable insight into how temperature-dependent changes in structure affect the charge carrier dynamics in FA-rich perovskites.

The preferential orientation of the perovskite (PVK) is typically accomplished by manipulation of the mixed cation/halide composition of the solution used for wet processing. However, for PVKs grown by thermal evaporation, this has been rarely addressed. It is unclear how variation in crystal orientation affects the optoelectronic properties of thermally evaporated films, including the charge carrier mobility, lifetime, and trap densities. In this study, we use different intermediate annealing temperatures Tinter between two sequential evaporation cycles to control the Cs0.15FA0.85PbI2.85Br0.15 orientation of the final PVK layer. XRD and 2D-XRD measurements reveal that when using no intermediate annealing primarily the (110) orientation is obtained, while when using Tinter = 100 °C a nearly isotropic orientation is found. Most interestingly for Tinter > 130 °C a highly oriented PVK (100) is formed. We found that although bulk electronic properties like photoconductivity are independent of the preferential orientation, surface related properties differ substantially. The highly oriented PVK (100) exhibits improved photoluminescence in terms of yield and lifetime. In addition, high spatial resolution mappings of the contact potential difference (CPD) as measured by KPFM for the highly oriented PVK show a more homogeneous surface potential distribution than those of the nonoriented PVK. These observations suggest that a highly oriented growth of thermally evaporated PVK is preferred to improve the charge extraction at the device level.

Co-evaporation of metal halide perovskites by thermal evaporation is an attractive method since it does not require harmful solvents and enables precise control of the film thickness. Furthermore, the ability to manipulate the Fermi level allows the formation of a graded homojunction, providing interesting opportunities to improve the charge carrier collection efficiency. However, little is known about how these properties affect the charge carrier dynamics. In this work, the structural and optoelectronic properties of co-evaporated MAPbI3 films varying in thickness (100, 400, and 750 nm) with a gradient in composition are analyzed. The X-ray diffraction patterns show that excess PbI2 is only present in the thick layers. From X-ray photoelectron spectroscopy depth analysis, the I/Pb atomic ratio indicates methylammonium iodide deficiencies that become more prominent with thicker films, resulting in differently n-doped regions across the thick MAPbI3 films. We suggest that due to these differently n-doped regimes, an internal electric field is formed. Side-selective time-resolved microwave photo conductivity measurements show an elongation of the charge carrier lifetimes on increasing thickness. These observations can be explained by the fact that excess carriers separate under the influence of the electric field, preventing rapid decay in the thick films.