We investigate the structural and quantum transport properties of isotopically enriched Si28/SiO228 stacks deposited on 300-mm Si wafers in an industrial CMOS fab. Highly uniform films are obtained with an isotopic purity greater than 99.92%. Hall-bar transistors with an oxide stack comprising 10 nm of Si28O2 and 17 nm of Al2O3 (equivalent oxide thickness of 17 nm) are fabricated in an academic cleanroom. A critical density for conduction of 1.75×1011cm-2 and a peak mobility of 9800cm2/Vs are measured at a temperature of 1.7 K. The Si28/SiO228 interface is characterized by a roughness of Δ=0.4nm and a correlation length of Λ=3.4nm. An upper bound for valley splitting energy of 480μeV is estimated at an effective electric field of 9.5 MV/m. These results support the use of wafer-scale Si28/SiO228 as a promising material platform to manufacture industrial spin qubits.

Quantum computing's value proposition of an exponential speedup in computing power for certain applications has propelled a vast array of research across the globe. While several different physical implementations of device level qubits are being investigated, semiconductor spin qubits have many similarities to scaled transistors. In this article, we discuss the device/integration of full 300mm based spin qubit devices. This includes the development of (i) a ²⁸ Si epitaxial module ecosystem for growing isotopically pure substrates with among the best Hall mobility at these oxide thicknesses, (ii) a custom 300mm qubit testchip and integration/device line, and (iii) a novel dual nested gate integration process for creating quantum dots.